ITAST (Iranian Textile Association of Science and Technology) Journal of Textiles and Polymers 2322-5203 7 2 2019 06 01 Flame-Retardant Cellulosic Fiber Nanocomposite Based on Aluminum Tetraborate and Aluminum Tungstate Flame-Retardant Cellulosic Fiber Nanocomposite Based on Aluminum Tetraborate and Aluminum Tungstate 3 12 92112 EN Shohreh Fakouri Nav Department of Chemistry, Faculty of Science, University of Guilan, Rasht, Iran Hadi Fallah Moafi Department of Chemistry, Faculty of Science, University of Guilan, Rasht, Iran Journal Article 2019 08 18 Nanoaluminum tetraborate (Al2(B4O7)3) and nanoaluminum tungstate (Al2(WO3)3) were prepared by in situ precipitation method on the surface of cellulosic fibers to achieve flame retardant nanocomposite fibers. The prepared nanocomposite fibers were characterized by several techniques such as XRD, SEM, TEM, EDS, and FTIR. Al2(B4O7)3 and Al2(WO3)3 with less than 100 nm in size were dispersed throughout on the surface of the fibers without the formation of large aggregates which showed effective flame retardancy properties. It was found that loading 2.60% Al2(B4O7)3 and 4.95% Al2(WO3)3 onto the cellulosic fibers improved greatly the flame retardancy behavior of  nanocomposite fibers which was approved by vertical flame test and limiting oxygen index (LOI) values. The thermal stability and amount of heat release of untreated and flame retardant fibers were evaluated by thermogravimetric (TGA) and differential scanning calorimetry (DSC) analyses. The results showed that the flame retardancy mechanism of the obtained flame retardant nanocomposite fibers probably is a condensed-phase phenomenon due to the formation of a protective char layer that acts as a mass transport barrier and a thermal insulator. http://www.itast.ir/article_92112_a48318c32dbfabe437e06652608297f5.pdf